Title: Evolution of nano-size precipitates during tempering of 9Cr-1Mo-1W-V-Nb steel and their influence on mechanical properties
Authors: Saini N.
Pandey C.
Mahapatra M.M.
Mulik R.S.
Keywords: Micro-hardness
Nano-size precipitates
P911 steel
Tempering temperature
Issue Date: 2018
Citation: 8
Abstract: The aim of the characterization of P911 steel is to determine the consequence of different tempering temperature on nano-size particle evolution and their effect on the mechanical properties. P911 steel was normalized at 1040 �C for 1 h and subjected to varying tempering condition in the range of 720�800 �C for 2 h of tempering time. To study the effect of tempering temperature on nano-size particles distribution and grain size of P911 steel, field-emission scanning electron microscope (FESEM) and optical microscope (OM) were utilized. The other tests were hardness measurement and room-temperature tensile testing was performed to characterize the P911 steel for different tempering condition. The ultimate tensile strength (UTS) and hardness have found a great dependency on the area fraction of precipitates present in the microstructure. The UTS and hardness were observed to be increased continuously with increase in tempering temperature in range of 720�800 �C. � 2017 Elsevier B.V.
Appears in Collections:Research Publications

Files in This Item:
There are no files associated with this item.

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.