Title: A brief study on ?-ferrite evolution in dissimilar P91 and P92 steel weld joint and their effect on mechanical properties
Authors: Pandey C.
Mahapatra M.M.
Kumar P.
Saini N.
Thakre J.G.
Vidyarthy R.S.
Narang H.K.
Keywords: A-TIG
Charpy toughness
GTAW
Hardness
?-Ferrite
Issue Date: 2018
Citation: 19
Abstract: Ferritic/martensitic 9Cr-1Mo-V-Nb steel also designated as ASTM A335 used in construction of several components of power plants operating in temperature range of 600�650 �C. In present investigation, dissimilar weld joint of P91 and P92 steel were prepared using the autogenous tungsten inert gas (A-TIG) welding and multi-pass gas tungsten arc welding (GTAW) process. A comparative study was performed on evolution of ?-ferrite patches in weld fusion zone and heat affected zones (HAZs) of welded joints. The evolution of ?-ferrite patches was studied in as-welded and post-weld heat treatment (PWHT) condition. PWHT was carried out at 760 �C for tempering time of 2 h and 6 h, for both A-TIG and GTA weld joints. It was observed that presence of higher content of ferrite stabilizer in P92 steel promote the formation of ?-ferrite patches in weld fusion zone as well as HAZs. To study the effect of welding process and PWHT, Charpy V impact energy and microhardness tests were performed. For microstructure characterization, field-emission scanning electron microscope (FESEM) and optical microscope were utilized. � 2017 Politechnika Wroc?awska
URI: http://dx.doi.org/10.1016/j.acme.2017.12.002
http://10.10.32.48:8080/jspui/handle/2008/1797
Appears in Collections:Research Publications

Files in This Item:
There are no files associated with this item.


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.