Title: Characterization of microstructure of HAZs in as-welded and service condition of P91 pipe weldments
Authors: Pandey C.
Giri A.
Mahapatra M.M.
Kumar P.
Keywords: grain boundary
microstructure
scanning electron microscopy (SEM)
tempering
toughness
Issue Date: 2017
Citation: 34
Abstract: Steels 9-12% Cr, having the high creep rupture strength are advocated for the modern low polluting thermal power plants. In the present investigation, the P91 pipe weldments have been characterized for microstructural responses in as-welded, post-weld heat treatment (PWHT) and ageing conditions. The PWHT of welded samples were carried out at 760 �C for time of 2 h and ageing at 760 �C for 720 h and 1440 h, respectively. The effect of time has been studied on precipitates size, distribution of precipitates and grain sizes present in various zones of P91 steel weldments. The impact toughness and hardness variation of heat affected zone (HAZ) have also been studied in as-welded condition as well as at different heat treatment condition. A significant change was observed in grain size and precipitates size after each heat treatment condition. The maximum impact toughness of HAZ was obtained after PWHT at 760 �C for 2 h. The main phase observed in weld fusion zone in as-welded, PWHT and ageing conditions were M23C6, MX, M7C3, Fe-rich M3C and M2C. The unwanted Z-phase (NbCrN) was also noticed in weld fusion zone after ageing of 1440 h. � 2017, The Korean Institute of Metals and Materials and Springer Science+Business Media Dordrecht.
URI: http://dx.doi.org/10.1007/s12540-017-6394-5
http://10.10.32.48:8080/jspui/handle/2008/1563
Appears in Collections:Research Publications

Files in This Item:
There are no files associated with this item.


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.