|Title:||Effect of normalization and tempering on microstructure and mechanical properties of V-groove and narrow-groove P91 pipe weldments|
|Abstract:||In Very High Temperature Reactor (VHTR), The Nb-V modified 9Cr-1Mo (P91) creep strength enhanced ferritic (CSEF) steel is currently considered as a candidate material for reactor internals and reactor pressure vessels (RPVs). After the welding of P91 steel, the inhomogeneous microstructure of weldment is a serious issue because it promotes the well-known Type IV cracking in P91 weldments. The present research work is focused on how the microstructure evolve in various zone of P91 pipe weldment during the sub-critical post weld heat treatment (PWHT) and normalized and tempered (N&T) heat treatment. The effect of PWHT and N&T heat treatment are also considered on tensile properties and hardness variation of P91 weldments. To characterize the sample scanning electron microscope (SEM), X-ray diffraction (XRD) and optical micrograph was used. It was observed that the N&T heat treatment provides the homogeneous microstructure compared to PWHT. The superior mechanical properties was also measured in N&T condition compared to PWHT. Study of fracture surface morphology of tensile tested specimen in different heat treatment condition is also presented. � 2017 Elsevier B.V.|
|Appears in Collections:||Research Publications|
Files in This Item:
There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.