Title: Effect of diffusible hydrogen content on embrittlement of P92 steel
Authors: Saini N.
Pandey C.
Mahapatra M.M.
Keywords: Diffusible hydrogen
Heat affected zone
Hydrogen assisted cracking
Implant test
Lower critical stress
P92 steel
Issue Date: 2017
Citation: 13
Abstract: In the present investigation, varying electrode conditions (dried and contaminated) have been employed during welding of P92 steel to study the effect of diffusible hydrogen level on hydrogen-assisted cracking (HAC). Shielded metal arc welding process was employed to deposit the metal on a P92 steel plate. To evaluate HAC, the Granjon implant test with varying diffusible hydrogen content in the deposited metal was utilized. The diffusible hydrogen level was measured in the deposited metal by using the mercury method. Lower critical stress (LCS), embrittlement index (EI) and normalized critical stress ratio were evaluated from the Granjon implant test. The fracture surface morphology of fractured implant specimens has been studied by using a field emission secondary electron microscope. The P92 steel plate welded by the contaminated electrode with a high level of diffusible hydrogen was found to be more susceptible to HAC. As diffusible hydrogen content increased in the deposited metal, the LCS value and EI were observed to be decreased. � 2017 Hydrogen Energy Publications LLC
URI: http://dx.doi.org/10.1016/j.ijhydene.2017.05.214
http://10.10.32.48:8080/jspui/handle/2008/1393
Appears in Collections:Research Publications

Files in This Item:
There are no files associated with this item.


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.